| Shapes | Round, Rectangular, Square, Hydraulic, Straight, "U" Shape, Coiled, Honed Tubes, Pan Cake Coils |
| Manufacturing Type | Seamless / ERW / Welded / Fabricated / CDW / CDS / DOM / CEW / 100% X Ray Welded |
| Delivery Condition | Annealed and Pickled (AP), Polished, Bright Annealed (BA), Cold Drawn, MF |
| Surface Finish | BA, 2B, No.4, No.1, No.3, No.8, 8K, HL, 2D, 1D, Mirror Polished, 180G, 320G, 400G Satin/ Hairline, 400G, 500G, 600G or 800G Mirror finish Tubing or Custom Finish as per customer's specification |
| Thickness Range | SCH 5, SCH10, SCH 40, SCH 80, SCH 80S, SCH 160, SCH XXH, SCH XXS, SCH XS |
| Standard | SUS, JIS, AISI, ASTM, GB, DIN, EN |
| Relevant Standard | ASTM A213, ASTM A312, ASTM A269, ASTM A778, ASTM A554, ASTM A249, ASTM A269, ASTM A270, ASTM A789, DIN 17456, DIN17457, DIN 17459, JIS G3459, JIS G3463, GOST9941, EN10216, BS3605, GB13296 |
| Value Added Services |
|
| Swg & Bwg | 10 Swg., 12 Swg., 14 Swg., 16 Swg., 18 Swg., 20 Swg. |
| END | Plain End, Beveled End, Treaded |
| Processing Service | Bending, Welding, Decoiling, Punching, Cutting, Moulding |
| Technique | Cold drawn, Cold rolled, Hot rolled, Extrusion Tube |
|
ASTM
|
A312, A376,A358, A269, A249, A403, A182, A351 |
|
ASME
|
SA312, SA376, Pressure SA358,SA269, SA249,SA403, SA182, SA351 |
| GRADE |
C
|
MN
|
SI
|
P
|
S
|
CR
|
MO
|
NI
|
N
|
|
|---|---|---|---|---|---|---|---|---|---|---|
|
316L
|
Min
|
-
|
-
|
-
|
-
|
-
|
16.0
|
2.00
|
10.0
|
-
|
|
Max
|
0.03
|
2.0
|
0.75
|
0.045
|
0.03
|
18.0
|
3.00
|
14.0
|
0.10
|
| GRADE | TENSILE STR (MPA) MIN |
YIELD STR 0.2% PROOF (MPA) MIN |
ELONG (% IN 50MM) MIN |
HARDNESS | |
|---|---|---|---|---|---|
| ROCKWELL B (HR B) MAX | BRINELL (HB) MAX | ||||
|
316L
|
485
|
170
|
40
|
95
|
217
|
| GRADE | DENSITY (KG/M3) |
ELASTIC MODULUS (GPA) |
MEAN CO-EFF OF THERMAL EXPANSION (ΜM/M/°C) | THERMAL CONDUCTIVITY (W/M.K) |
SPECIFIC HEAT 0-100°C (J/KG.K) |
ELEC RESISTIVITY (NΩ.M) |
|||
|---|---|---|---|---|---|---|---|---|---|
| 0-100°C | 0-315°C | 0-538°C | AT 100°C | AT 500°C | |||||
| 316L | 8000 | 193 | 15.9 | 16.2 | 17.5 | 16.3 | 21.5 | 500 | 74 |
|
GRADE
|
UNS
NO |
OLD BRITISH
|
EURONORM
|
SWEDISH
SS |
JAPANESE
JIS |
||
|---|---|---|---|---|---|---|---|
|
BS
|
EN
|
NO
|
NAME
|
||||
|
316L
|
S31603
|
316S11
|
-
|
1.4404
|
X2CrNiMo17-12-2
|
2348
|
SUS 316L
|
Polishing |
polish nearly any stainless steel pipe item to a #4 polish, #6 Polish, #7 polish or a #8 mirror finish. Stainless steel polished pipes can also be cut to size. |
Beveling |
bevel stainless steel pipe to prepare for welding or other processes. |
Honing/Turning |
hone pipe and tube, using a precision abrasion process in order to obtain a desired finish or close dimensional tolerance. |
Heatreating & Annealing |
Some grades of stainless steel pipe and tube can be heatreated to change the mechanical properties. Precipitation Hardening Stainless Steels such as 17-4PH can be heatreated. In some cases, secondary annealing 300 series stainless steel may be required depending on the application |
Positive Material Identification (PMI) |
Shengtian Group can perform PMI testing in house for most stainless steel grades, or we can work with independent labs to complete PMI in order to meet customer specifications. |
UT Testing |
In some cases, UT testing of the stainless steel pipe and tueb may be required. We can assist you with this requirement. |