ASTM A210 This specification covers seamless medium-carbon steel boiler and superheater tubes. The specification also covers minimum-wall-thickness, tubing sizes, boiler flues including safe ends, arch and stay tubes. The specification provides tensile and hardness properties but only applicable to certain size limitations. Material manufacturing shall be killed. Tubes shall be made by seamless process, marked as either hot-finished or cold-finished. Surface condition shall be specifically stated in the order. Chemical composition shall conform to the requirements. Elemental composition other than listed here shall not be permitted. Tension test, flattening test, flaring test, hardness test, hydrostatic or nondestructive electric test shall be made on specimens. Superheater tubes shall be formed without defects and shall withstand expansion, beading, forging, welding, and bending.
ASTM A210 is the standard covers seamless medium-carbon steel boiler and superheater tubes. Seamless medium carbon steel pipe for boiler tube and boiler flue pipe, including a minimum wall thickness of the security side, the dome and the support tube and superheater tubes.
ASTM A210 Pipes Application
For high, middle, low pressure boiler and pressure purpose
ASTM A210 / A210M Flattening Test
One flattening test shall be made on specimens from each end of one finished tube from each lot, but not the one used for the flaring test. Tears or breaks occurring at the 12 or 6 o’clock positions on Grade C tubing with sizes of 2.375 in. [60.3 mm] in outside diameter and smaller shall not be considered a basis for rejection.
ASTM A210 / A210M Flaring Test
One flaring test shall be made on specie- men from each end of the one finished tube from each lot, but not the one used for the flattening test.
Ordering Information
Orders for ASTM A210 / A210M, ASME SA210 should include the following, as required, to describe the desired material adequately:
Quantity (feet, meters, or number of lengths),
Name of material (seamless pipes),
Grade,
Manufacture (hot-finished or cold-finished),
Size (outside diameter and minimum wall thickness),
Length (specific or random),
Optional requirements,
Test report required (see section on Certification of Specification A 450/A 450M),
Specification designation,
Special requirements.
When these products are to be used in applications conforming to ISO Recommendations for Boiler Construction, the requirements of Specification ASTM A 520 , shall supplement and supersede the requirements of this specification.
| Steel Grade | C | Si | Mn | S | P |
| A210 A1/ SA-210A1 | ≤0.27 | ≥0.10 | ≤0.93 | 0.020 | 0.025 |
| A210C/ SA-210C | ≤0.35 | ≥0.10 | 0.29-1.06 | 0.020 | 0.025 |
| Grade | Tensile strength (Mpa) |
Yield point(Mpa) not less than |
Elongation(%) not less than |
Impact(J) not less than |
Hardness not less than |
| A210 A1/ SA-210A1 | ≥415 | 255 | " | 79HRB | |
| A210C/ SA-210C | ≥485 | 275 | " | 89HRB |
| Hot rolled | Outside Diameter, mm | Tolerance, mm |
| OD≤101.6 | +0.4/-0.8 | |
| 101.6＜OD≤127 | +0.4/-1.2 | |
| Cold Drawn | Outside Diameter, mm | Tolerance, mm |
| OD＜25.4 | ±0.10 | |
| 25.4≤OD≤38.1 | ±0.15 | |
| 38.1＜OD＜50.8 | ±0.20 | |
| 50.8≤OD＜63.5 | ±0.25 | |
| 63.5≤OD＜76.2 | ±0.30 | |
| 76.2≤OD≤101.6 | ±0.38 | |
| 101.6＜OD≤127 | +0.38/-0.64 |
| Hot rolled | Outside Diameter , mm | Tolerance, % |
| OD≤101.6, WT≤2.4 | +40/-0 | |
| OD≤101.6, 2.4＜WT≤3.8 | +35/-0 | |
| OD≤101.6, 3.8＜WT≤4.6 | +33/-0 | |
| OD≤101.6, WT>4.6 | +28/-0 | |
| OD>101.6, 2.4＜WT≤3.8 | +35/-0 | |
| OD>101.6, 3.8＜WT≤4.6 | +33/-0 | |
| OD>101.6, WT>4.6 | +28/-0 | |
| Cold Drawn | Outside Diameter , mm | Tolerance, % |
| OD≤38.1 | +20/-0 | |
| OD>38.1 | +22/-0 |
| Method of Manufacture |
Outside Diameter, in. [mm] |
Cut Length,in. [mm] | |
| Over | Under | ||
| Seamless, hot-finished | All sizes | 3 ⁄ 16 [5] | 0 [0] |
| Seamless, cold-finished | Under 2 [50.8] | 1 ⁄ 8 [3] | 0 [0] |
| 2 [50.8] and over | 3 ⁄ 16 [5] | 0 [0] | |
| 2 [50.8] and over | 3 ⁄ 16 [5] | 0 [0] | |
Both ends of each crate will indicate the order no., heat no., dimensions, weight and bundles or as requested.
(1)Tension Test—One tension test shall be made on a specimen for lots of not more than 50 tubes. Tension tests shall be made on specimens from two tubes for lots of more than 50 tubes.
(2)Flattening Test—One flattening test shall be made on specimens from each end of one finished tube from each lot.
(3)Flaring Test—One flaring test shall be made on speci- mens from each end of the one finished tube from each lot.
(4)Hardness Test—Brinell or Rockwell hardness tests shall be made on specimens from two tubes from each lot.
(5)Hydrostatic or Nondestructive Electric Test—Each tube shall be subjected to the hydrostatic.
One flattening test shall be made on specimens from each end of one finished tube from each lot, but not the one used for the flaring test. Tears or breaks occurring at the 12 or 6 o’clock positions on Grade C tubing with sizes of 2.375 in. [60.3 mm] in outside diameter and smaller shall not be considered a basis for rejection.
One flaring test shall be made on specie- men from each end of the one finished tube from each lot, but not the one used for the flattening test.
ASTM A210 seamless medium carbon steel boiler and superheater tubes are medium carbon steel Seamless Tubing used in boilers, boiler flues, super heaters.